| dc.description.abstract |
Aluminum casting results are still many that suffered damage. Some of the causes are the lack of permeability and print strength. This research was expected to be able to know the capability of casting product to impact load from various temperature which was measured and expected to increase productivity of castings result. This research was expected to know the ability of casting products to the torque load of various forces that were measured and expected to increase the productivity of the castings. This research used variation of permeability value by testing 3 materials tested with the same length and diameter. This study was conducted by observing the effect of corner and force of torque on the breaking strength performed by torque testing with the first test of the force of 4.6 ton with the angle 20 with the fracture period at 70 0 with the corner 0 ton, test the two force of 4.6 ton with corner 20 with fracture at 0 ton with corner 70 0, third test of force 3 ton with corner 2 (More) | en_US |
| dc.language.iso | en | en_US |
| dc.publisher | Universitas Harapan Medan | en_US |
| dc.subject | silicon aluminum material based on fracture period in torque test | en_US |
| dc.title | Analysis Characteristics of Silicon Aluminum Material based on Fracture Period in Torque Test | en_US |
| dc.type | Prosiding | en_US |