PENGARUH EXPOSURETIME TERHADAP PANJANG RETAK MATERIAL BAJA NIRKARAT AUSTENIT AISI 304,316 DAN 316L YANG MENGALAMI KEGAGALAN STRESS COROSION CRACKING
junaidi ,dn.adnyana () 2013This research was carried out by first testing using the Spring Loaded Fixture type in accordance with ASTM G49 and E 292 for the experimental method and specimen geometry respectively. Initiation of SCC failure begins with pitting corrosion and thinning attacks to date stress reaches the highest strength Furthermore, in this case the aim was to determine the characteristics of failure of SCC Austenitic stainless steel AISI 304, AISI 316, and 316L in Glycerol solution with four variations of chloride concentration, namely 50, 6,000, 9,000, and 12,000 ppm, two types of initial tensile stress, namely 50 % and 70% Yield Strength from each material test, and 150 oC constant temperature.Failure occurs in catastrophic and brittle (transgranular) fractures. AISI 304 is more vulnerable to all experimental conditions. All material tests did not fail for 50 ppm chloride concentration up to 556 hours of exposure time. The more concentration and chloride concentration is given, the crack speed becomes higher by shortening the failure time.
Analisa Pengaruh Media Pendingin dan Pemanasan Terhadap Kekerasan dan Struktur Mikro Pada Proses Tempering Baja Perkakas SKD 11.
budi santri kusuma ,junaidi () 2014Perlakuan panas mempunyai khasiat untuk meningkatkan tegangan, menghaluskan butiran kristal, meningkatkan kekerasan, meningkatkan tegangan jatuh logam. Penelitian ini bertujuan untuk meningkatkan kualitas baja SKD 11 Stainess Steel milik SKD 11 ALAT BAJA DENGAN Karbon dan kromium tinggi, paduan dengan lainnya unsur yaitu vanadium dan molibdenum sebagian besar baja skd 11 digunakan pada peralatan yang memerlukan ketahanan aus yang tinggi. Sebagian besar baja skd 11 digunakan untuk proses pengerjaan dingin (cold working) contoh proses blanking dies dan machining. Karena adanya proses pengerasan pada baja SKD 11 timbul tegangan dan rapuh sehingga dalam pemupukan harus dilakukan proses fuether,tempering.Baja SKD11 mendapat perlakuan pemanasan,suhu pengerasan 12000C,hasil uji kekerasan antara 167 s/d 232,2 HV.
Analisa Pengaruh Media Pendingin dan Pemanasan Terhadap Kekerasan dan Struktur Mikro Pada Proses Tempering Baja Perkakas SKD 11.
budi santri kusuma ,junaidi () 2014Heat treatment has a good to increase tension ,refline crystal grains,increasing violence,increasing the volltage drop of metals.This Study aims to improve the quality of steel SKD 11 Stainess Steel belong SKD 11 TOOL STEEL WITH Carbon and high chromium,alloys with other elements that vanadium and molybdenum most of skd 11 steel used in appliances that require high wear resistance.Most of skd 11 Steel used for cold working process ( cold working ) example of blanking dies and machining proceses.Due to the process of hardening of the steel SKD 11 ,the tension arises and fragile ,so the fertilizer is to be done fuether process,tempering.Steel SKD11 received treat heating,hardening temperatures 12000C,Hardeness test results between 167 to 232,2 HV.
Analisa Pahat Potong (HSS ) dengan Material Besi Cor Pada Mesin Bubut Universal
junaidi () 2015Alat pemotong adalah alat bubut. Proses Pemotongan Alat HSS Dengan Bahan Bubut Universal Cast Iron yang umum dijumpai pada Analisis Proses pemotongan berdasarkan beberapa aspek yaitu Gaya Pemotongan, Kecepatan Pemotongan, Daya Pemotongan, Pemotongan Daya Indikasi, Zona Temperatur 1 dan Zona Temperatur 2. Tujuan Penelitian ini adalah untuk mengetahui seberapa besar pemotongan yang dilakukan. Kecepatan, Daya Pemotongan, Daya Motor Listrik, Temperatur Zona 1 dan Temperatur Zona 2 yang menggerakkan HSS pemotongan pahat di Proses Pembubutan Material Besi Cor. Gaya potong diperoleh dari analisa gambar hubungan antara yang direkomendasikan Komponen Gaya Potong dengan bidang potong dan Kecepatan Potong diperoleh dari gambar analisa hubungan antar laju Pakan Kecepatan Pemotongan yang direkomendasikan
Analysis Cutting Tool High Speed Steel ( HSS ) with Cast Iron Material From Universal Lathe
junaidi* ,darmawati ,ahmad yanie () 2015Alat potong merupakan alat mesin bubut. Alat proses pemotongan KARBIDA dengan Bahan Besi Cor Mesin Bubut Universal yang umum dijumpai pada Analisa Proses Pemotongan ditinjau dari beberapa aspek yaitu Gaya Potong, Kecepatan Potong, Daya Potong, Daya Indikasi Pemotongan, Zona Temperatur 1 dan Zona Temperatur 2. Tujuan Tujuan dari penelitian ini adalah untuk mengetahui seberapa besar Kecepatan Potong, Daya Potong, Daya Motor Listrik, Temperatur Zona 1 dan Temperatur Zona 2 yang menggerakkan pahat potong HSS pada Proses pembubutan Material Besi Cor. Gaya potong diperoleh dari analisis gambar hubungan antara Komponen Gaya Potong yang direkomendasikan dengan bidang potong dan Kecepatan Pemotongan diperoleh dari analisis gambar hubungan antara laju Pengumpanan Kecepatan Pemotongan yang direkomendasikan.